Film morphology:

Samples
N of monolayers CP-HCA-1 CP-HCA-2 CP-BCA
12 1 sample 1 sample 1 sample
24 2 samples 1 sample 1 sample
48 1 sample 1 sample 1 sample
Substrates: glass plates 126 126 mm in size coated by Cr films 150 nm thick

Microphotograph of 48 monolayers of CP-HCA-1 deposited by Langmuir-Schaefer technique onto glass plates with chromium coatings

Results
Density of point-like defects (cm-2) (magnifications up to 1000)
Bright field mode
25 - 30
Dark field mode
200 - 250